L.M Shaft Plating Rod
Material : KS.STB-2(JIS:SUJ-2)High-frequency Quenching : -Hardness : HRC 60-64Hardening Layer : 0.8mm~3mmSurface Roughness : 1.5µmRmax BelowD.Tolerance : g6(g5)Chrome layer : 0.015mm~0.03mm
It is exclusively used for ball bush, suitable and economical in case of rust environment or bad working conditions.
Products
-
Heat treated plating rod
Material : S45CSurface Roughness : below 0.8SD.Tolerance : f6(f8)Straightness : below 0.2mm/1mHardness : HRC 55-60Chrome layer : 0.015mm~0.03mm
High frequency heat treatment:Hard Chromium Plating Shaft for rust resistance
Products Table
*Other products will be subject to the specific order. (Unit m/m)*(See standard
-
Hollow shaft plating rodPart of vehicle
Material : STB-2(JIS:SUJ-2)High-frequency Quenching : -Hardness : HRC 60-64Hardening Layer : 0.8mm~3mmSurface Roughness : 1.5µmRmax BelowD.Tolerance : g6(g5)Chrome layer : 0.015mm~0.03mm
It is exclusively used for ball bush shaft in hard chromium plating for resisting the corrosion of outer
-
Plating rodAuto machine part
Material : S45CSurface Roughness : below 0.8SD.Tolerance : f8Straightness : below 0.2mm/1mChrome layer : 0.015mm~0.03mm
It is suitable and economical in case of rust environment or bad working conditionsProduction of Hydraulic/Pneumatic Piston Rod and Automation Industry Field