HKRUB200 is the rubber for modeling after the pattern of a tire mold, which is used after mixing
with HKRUBK200. Due to its optimum viscosity, the complicated pattern of a tire mold can be
modeled after perfectly and the intermixing with bubbles has been minimized.
How to use
1. Mix HKRUB200 and HKRUBK200 in ratio of 100:14.
2. Mix by stirring them for at least 2 minutes, and especially pay attention to mixing well at bottom
and side of container.
3. If necessary, use releasing agent.
Curing
1. Full cure is completed after passing 16 hours at temperature of 25?.
2. If temperature is higher than 25?, curing speed is getting faster, and if lower, it is getting
slower..
3. Application should be done at more than 18?.
Physical properties
Test item
Measurement value
Test condition
Viscosity
HKRUB200
2,000 ~ 4,000
B/F #4 30rpm 25?
HKRUBK200
2,300 ~ 4,300
B/F #4 30rpm 25?
Hardness
21 ~ 38
KORI TYPE SA
Tensile strength
3.7~3.9kgf/cm2
LLOYD Co., LR 50K
Elongation
520~550%
LLOYD Co., LR 50K
Cautions
Use it after being fully aware of MSDS of HKRUB200.
1. Eye contact : Flush eyes with plenty of water or saline solution for 10-20 minutes until the
chemicals is removed thoroughly. Obtain medical attention without delay.
2. Skin contact: Wash skin with mild cleaning material or plenty of water for 10-20m minutes until
the chemicals is removed thoroughly. Obtain medical attention without delay.
3. Inhalation: Move person to fresh air, and if necessary, take artificial respiration. Obtain medical
attention without delay.
4. Ingestion: Wash out the stomach within 15 minutes and obtain medical attention without delay.
5. Note to physician: No specific antidote. Treatment of exposure should be directed at the control
of symptoms and the clinical condition of the patient.
? Tire Mold Manufacture Process – Casting Mold
? Tire Mold Patterning Rubber Using Method
Share HKRUB Series (Tire Mold Patterning Rubber) in Social Media